Stability comparison: A PCDTBT/PC71BM bulk-heterojunction versus a P3HT/PC71BM bulk-heterojunction

초록

In this study, the physical and chemical degradation behaviors of active layers based on semicrystalline p-type polymer (poly(3-hexylthiophene) (P3HT)) and [6,6]-phenyl C-71 butyric acid methyl-ester (PC71BM) are compared with the corresponding behaviors of amorphous p-type polymer of poly [N-9 ''-hepta-decanyl-2,7-carbazole-alt-5,5-(4',7'-di-2-thienyl-2',1',3'-benzothiadiazole)] (PCDTBT)and PC71BM. A surface morphological study of the active layer (from Atomic force microscopy (AFM) and scanning electron microscopy (SEM) images) and a chemical analysis (from X-ray photoelectron spectroscopy (XPS) and Energy dispersive X-ray spectroscopy (EDS) results) help explain why PCDTBT/PC71BM bulk heterojunction (BHJ) has a higher level of long-term stability under thermal and air stability experimental conditions than a P3HT/PC71BM-based BHJ. The power conversion efficiency for a PCDTBT/PC71BM BHJ cell and a P3HT/PC71BM BHJ cell decreased by 11% and 21%, respectively, after a thermal stability test and by 68% and 78%, respectively, after a 300 h air stability test. (C) 2012 Elsevier B.V. All rights reserved.

키워드